Diffusion Bonded Crystals are crystals consisting of two, three or more parts with different dopant levels. Usually, doped and undoped materials are used. Difussion Bonded Crystals are used to decrease thermal lensing effect considerably.This bonding technology in laser applications can not only greatly improve the laser performance and beam quatily, but also conducive to the intergration of laser systems and access to large-size crystal.
Product Presentation
Advantage:
Decrease thermal effect
Inprove efficiency
High damage threshold
Improve beam quality
Compact size
We can supply several assembly types as follows:
Material
Doping Concentration (atm) or Optical Density (cm-1)
Aperture (mm)
Length (mm)
YAG+Nd :YAG
0.6~1.2%
2×2~20×20
2~200
YAG+Cr4+ :YAG
0.6~7
2×2~20×20
2~50
Nd :YAG + Cr4+:YAG
0.6~1.2% / 0.6~7
2×2~20×20
2~200
YAG+Nd :YAG+YAG
0.6~1.2%
2×2~20×20
3~200
YAG+Nd:YAG+Cr4+:YAG
0.6~1.2% / 0.6~7
2×2~20×20
3~200
YAG+Nd:YAG+Cr4+:YAG+YAG
0.6~1.2% / 0.6~7
2×2~20×20
5~200
YAG+Cr4+:YAG+Nd:Ce:YAG+YAG
0.6~7/Nd:0.9~1.3%,Ce:Nd=1:10
2×2~10×10
5~130
YVO4+Nd:YVO4+YVO4
0.1~3%
2x2~10x10
1~20
YVO4+Nd:YVO4+YVO4
0.1~3%
Dia.2~10
3~20
Note:For other assembly type, please contact us for more information.
Specifications:
Damage
≤ 3.0 × 10 -3 cm-1
Flatness
< λ/10
Parallelism
≤ 10"
Perpendicularity
≤ 5 ′
Surface Quality
10/5 (MIL-O-13830A)
Optical Quality
Interference fringes ≤ 0.125/inch
Size
Diameter 2 ~ 18 mm, Length 3 ~ 200 mm
Dimensional tolerances
Diameter +0.000"/-0.05mm", Length ± 0.5mm“ Chamfer: <0.1 mm @ 45º
Coating
Upon request of customer
Environmental Suitability
I Cryo-Environment
a, Cro-Storage
Crystals in off- working state can be cryo-storaged. Sheet 5 Cryo-Storage-Test finds that crystal still works regularly after recoverying at room temperature
Sheet 5 Cryo-Storage Test
Test Item
Temperature
Time(hour)
Cryo-Storage
-55°
48
b,Cryo-Working
Sheet 6 Cryo-Working Test finds that crystal still works regularly when the temperature is summit of subzero-40 degree.
Sheet 6 Cryo-working Test
Test Item
Temperature (degree)
Time (hour)
Cryo-working
-40°
2
II, Hot-Environment
a, Hot-Storage
Crystals in off working state can be hot-storaged. Sheet 7 Hot-Storage Test finds that crystal still works regularly after recoverying at room temperature
Sheet 7 Hot-Storage Test
Test Item
Temperature (degree)
Time(hour)
Hot-Storage
70°
48
b,Hot-Working
Sheet 8 Hot-Working Test finds that crystal still works regularly when the temperature is summit of 60 degree.
Sheet 8 Cryo-working Test
Test Item
Temperature (degree)
Time (hour)
Cryo-working
60°
2
III Vibration-Environment
Crystals works regularly in the vibarant condition as Graph 1.
IV, Lashing (Basic Design)
Sheet 10 Lashing Test finds that crystals works regularly without any demage after being lashed.